Dynamic Considerations in Prediction of Fracture of Ultra High-Strength Steel During Crash

High strain rate response of automotive alloys (tensile + shearcharacterization):

1、DP980 (SMDI), DP600

2、Fully quenched Usibor? 1500-AS, Ductibor? 500-AS

Effect of strain rate on fracture?

1、Shear conditions (zero triaxiality)

2、Positive triaxiality conditions

Weld failure characterization – “spot weld groups”

? Achieves shear strains easily on the order of unity with relatively constant triaxiality of zero .

? Appropriate for high rate testing in Hopkinson bar or high speed hydraulics (1-1000/s).

Issue today lies in the majority of fracture characterization for crash CAE being doneat quasi-static rates…

Potential sources of rate effects:

? Elevated strain rates
? Temperature increase through adiabatic heating (~90% of plastic work convertedto heat) *
? Inertial effects

? Rate sensitivity is initially positive, but becomes negative atlarge strains
? Promotes earlier localization under shear loading

? Onset of shear cracking is determined as the point where thehardening rate is exhausted 1

? Repeatable and eliminates the need to detect fracture based on visible cracking 2

In tension, positive rate sensitivity promotes higher failure strains as strain rate increases.

In shear, thermal localizationreduces failure strain (as measuredusing DIC) with increasing strain rate.

? Given the coarse meshesnecessitated in vehicle CAE, failurestrains should be measured using alength scale on the order of theelement size

? DIC virtual strain gauge length: 0.3mm) versus 3-5 mm element size

? For these materials, shear strain tofailure input to FEA decreases withstrain rate!

? Less impact on positive triaxialityregime, however, confoundingresults exist in the literature

? Earlier localization,narrower thermal fieldfor the higher strengthconditions

? Thermal localizationenhanced for higherstrength alloys

? The strong workhardening of the DP600is clearly beneficial

? Interaction between nugget, HAZ and parent metal strength(single weld)

? Test method for weld group testing (Mode I Caiman)